BARRES EN ACIER RECTIFIÉS

Barres en acier au carbone C45 rectifié

Available profiles

RONDS: de 2 à 180 mm (sur demande en h6)

Specifications

Acciaio C45 - Steel C45

COMPOSIZIONE CHIMICA - CHEMICAL COMPOSITION (EN 10083-2:2006)

C% Si% Mn% P% S% Cr% Mo% Ni% Cr+Mo+Ni%
Min 0.42 - 0.50 - - - - - -
Max 0.50 0.40 0.80 0.045 0.045 0.40 0.10 0.40 0.63

CARATTERISTICHE MECCANICHE TRAFILATO +C - COLD-DRAWN MECHANICAL PROPERTIES +C (EN 10277-5:2008)

Spessore - Thickness
mm.
Rp0,2 min.
N/mm2
Rm (MinMax)
N/mm2
A%
Min
≥5≤10 565 7501050 5
>10≤16 500 7101030 6
>16≤40 410 6501000 7
>40≤63 360 630900 8
>63 310 580850 8

Download Trafital-C45.pdf


Acier allié 39 Ni Cr Mo 3 / 42 Cr Mo 4 pretraité rectifié

Available profiles

RONDS: de 6 à 160 mm (aussi supérieur sur demande)

Specifications

Acciaio 39 Ni Cr Mo 3 - Steel 39 Ni Cr Mo 3

COMPOSIZIONE CHIMICA - CHEMICAL COMPOSITION (EN 10277-5:2008)

C% Si% Mn% P% S% Cr% Mo% Ni%
Min 0.35 - 0.50 - - 0.60 0.15 0.70
Max 0.43 0.40 0.80 0.025 0.035 1.00 0.25 1.00

CARATTERISTICHE MECCANICHE LAMINATO ALLO STATO BONIFICATO +AR+QT - HOT ROLLED MECHANICAL PROPERTIES +AR+QT (EN 10083-3:2006)

Diametro - Diameter
mm.
Spessore - Thickness
mm.
Rp 0,2 min.
N/mm2
Rm (MinMax)
N/mm2
A%
Min
KV Min
J
Z%
Min
≤16 ≤8 785 9801180 11- 40
>16≤40 >8≤20 735 9301130 113540
>40≤100 >20≤60 685 8801080 124045
>100≤160>60≤100635 830980 124050
>160≤250>100≤160540 740880 134050

Acciaio 42 Cr Mo 4 - Steel 42 Cr Mo 4

COMPOSIZIONE CHIMICA - CHEMICAL COMPOSITION (EN 10083-3:2006)

C% Si% Mn% P% S% Cr% Mo%
Min 0.38 - 0.60 - - 0.90 0.15
Max 0.45 0.40 0.90 0.025 0.035 1.20 0.30

CARATTERISTICHE MECCANICHE LAMINATO ALLO STATO BONIFICATO +AR+QT - HOT ROLLED MECHANICAL PROPERTIES +AR+QT (EN 10083-3:2006)

Diametro - Diameter
mm.
Spessore - Thickness
mm.
Rp 0,2 min.
N/mm2
Rm (MinMax)
N/mm2
A%
Min
KV Min
J
Z%
Min
≤16 ≤8 900 11001300 10- 40
>16≤40 >8≤20 750 10001200 113545
>40≤100 >20≤60 650 9001100 123550
>100≤160>60≤100550 800950 133550
>160≤250>100≤160500 750900 143555